金属学报  2012, Vol. 48 Issue (1): 94-98    DOI: 10.3724/SP.J.1037.2011.00470

论文 本期目录 | 过刊浏览 |

具有超疏水表面的白铜在3.5%NaCl溶液中的电化学行为

徐群杰1, 2), 邓先钦1, 2), 潘红涛1, 2), 云虹1, 2)

1) 上海电力学院能源与环境工程学院上海高校电力腐蚀控制与应用电化学重点实验室, 上海 200090 2) 上海电力学院能源与环境工程学院上海热交换系统节能工程技术研究中心, 上海 200090

ELECTROCHEMICAL BEHAVIOR OF B30 Cu-Ni ALLOY WITH SUPER-HYDROPHOBIC SURFACE IN 3.5%NaCl SOLUTION

XU Qunjie1, 2),  DENG Xianqin1, 2),  PAN Hongtao1, 2), YUN Hong1, 2)

1) Key Laboratory of Shanghai Colleges and Universities for Corrosion Control in Electric Power System and Applied Electrochemistry, Institute of Energy and Environment Engineering, Shanghai University of Electric Power, Shanghai 200090 2) Shanghai Engineering Research Center of Energy-Saving in Heat Exchange Systems, Institute of Energy and Environment Engineering, Shanghai University of Electric Power, Shanghai 200090

徐群杰 邓先钦 潘红涛 云虹. 具有超疏水表面的白铜在3.5%NaCl溶液中的电化学行为[J]. 金属学报, 2012, 48(1): 94-98.
, , , , . ELECTROCHEMICAL BEHAVIOR OF B30 Cu-Ni ALLOY WITH SUPER-HYDROPHOBIC SURFACE IN 3.5%NaCl SOLUTION[J]. Acta Metall Sin, 2012, 48(1): 94-98.

摘要 参考文献 相关文章 Metrics 全文: PDF(885 KB)   摘要: 通过化学刻蚀法和自组装技术, 构建了白铜的超疏水表面. 利用接触角测试和电化学分析技术探讨了制备工艺对疏水膜性能的影响. 对不同刻蚀条件下制备的超疏水表面的电化学测试结果进行比较, 结果表明: 合适的表面粗糙结构是制备具有优良耐蚀性能的超疏水膜的关键. 接触角测量和电化学测试结果表明: 构建的白铜基超疏水表面的接触角可达152.8o, 该超疏水膜能够大幅提高白铜在3.5%NaCl溶液中的耐蚀性能, 缓蚀效率达到96.1%. 关键词 ： 白铜,  超疏水膜,  化学刻蚀,  自组装,  耐蚀性     Abstract：Super-hydrophobic surface has been considered a new and promising anti-corrosion technology, recently. A super-hydrophobic film has been fabricated on Cu-Ni alloy (B30) substrates by chemical etching and self-assembly. The effects of etching process and self-assembly technology on the property of filmed B30 had been investigated by means of contact angle measurement and electrochemical test. The results show that suitable surface roughness played a vital role in preparing super-hydrophobic surface with excellent corrosion resistance in comparison with the electrochemical test results of different hydrophobic B30 surface. Moreover, the results indicated that the corrosion resistance of B30 in 3.5%NaCl solution could greatly improved by the super-hydrophobic surface (contact angle 152.8o), and the inhibition efficiency reached 96.1%. Key words： Cu-Ni alloy    super-hydrophobic film    chemical etching    self-assembly    corrosion resistance 收稿日期: 2011-07-22      基金资助: 国家自然科学基金资助项目21003089 作者简介: 徐群杰, 男, 1969年生, 教授, 博士 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 徐群杰 邓先钦 陆章辉 潘红涛 云虹 44.8K 链接本文: https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00470      或      https://www.ams.org.cn/CN/Y2012/V48/I1/94 [1] Chen H, Yin R H, Wan Z Y. Corros Sci, 2008; 50: 3527 [2] Wan Z, Zhang L, Yin R H. Acta Metall Sin, 2008; 2: 203 (万宗跃, 张利, 印仁和. 金属学报, 2008; 2: 203) [3] Xu Q J, Zhu L J, Qi H. Acta Metall Sin, 2008; 44: 1360 (徐群杰, 朱律均, 齐 航. 金属学报, 2008; 44: 1360) [4] Xu Q J, Zhu L J, Cao W M. Acta Phys–Chim Sin, 2008; 24: 1724 (徐群杰, 朱律均, 曹为民. 物理化学学报, 2008; 24: 1724) [5] Guo L, Yuan W, Li J. Appl Surf Sci, 2008; 254: 2158 [6] Chen L J, Chen M, Zhou H D. Appl Surf Sci, 2008; 255: 3459 [7] Wang P, Qiu R, Zhang D. Electrochim Acta, 2010; 56: 517 [8] Ishizaki T, Hieda J, Saito N. Electrochim Acta, 2010; 55: 7094 [9] He T, Wang Y, Zhang Y. Corros Sci, 2009; 51: 1757 [10] Qian B T, Shen Z Q. Langmuir, 2005; 21: 9007 [11] Liu T, Yin Y S, Chen S G. Electrochim Acta, 2007; 52: 3709 [12] Sarkar D K, Farzaneh M, Paynter R W. Appl Surf Sci, 2010; 256: 3698 [13] Tsougeni K, Vourdas N, Tserepi A. Langmuir, 2009; 25: 11748 [14] Li S M, Zhou S Z, Liu J H. Acta Phys–Chim Sin, 2009; 25: 2581 (李松梅, 周思卓, 刘建华. 物理化学学报, 2009; 25: 2581) [15] Zhang Q, Zhu Y R, Huang Z Y. Chem J Chin Univ, 2009; 30: 2210 (张芹, 朱元荣, 黄志勇. 高等学校化学学报, 2009; 30: 2210) [16] Yang H, Pi P, Cai Z. Appl Surf Sci, 2010; 256: 4095 [17] Wu X, Zheng L, Wu D. Langmuir, 2005; 21: 2665 [18] Kato C, Castle J E, Ateya B C, Pickexing H W. J Electrochem Soc, 1980; 127: 1897 [19] Li Y F, Yu Z J, Yu Y F. J Chem Ind Eng (China), 2008; 22: 6 (李艳峰, 于志家, 于跃飞. 高等化学工程学报, 2008; 22: 6) [20] Gu C D, Ren H, Tu J P. Langmuir, 2009; 25: 12299 [21] Liao Q Q, Yue Z W, Zhu Z W. Acta Phys–Chim Sin, 2009; 25: 1655 (廖强强, 岳忠文, 朱忠伟. 物理化学学报, 2009; 25: 1655) [22] Fu X Y, He X H. Appl Surf Sci, 2008; 255: 1776 [23] Cassie A B, Bxater S. Faraday Soc, 1944; 40: 546 [24] Liu T, Liu T, Chen S G. Chin J Inorg Chem, 2008; 24: 1859 (刘通, 刘涛, 陈守刚. 无机化学学报, 2008; 24: 1859) [25] Liu T, Chen S G, Cheng S. Electrochim Acta, 2007; 52: 8003 [1] 许林杰, 刘徽, 任玲, 杨柯. Cu对Ni-Ti合金抗支架内再狭窄与耐蚀性能的影响[J]. 金属学报, 2023, 59(4): 577-584. [2] 黄一川, 王清, 张爽, 董闯, 吴爱民, 林国强. 用于燃料电池双极板的不锈钢成分优化[J]. 金属学报, 2021, 57(5): 651-664. [3] 黄松鹏, 彭灿, 曹公望, 王振尧. 受BTA保护的白铜在模拟工业大气环境中的腐蚀行为[J]. 金属学报, 2021, 57(3): 317-326. [4] 王雪梅, 殷正正, 于晓彤, 邹玉红, 曾荣昌. AZ31镁合金表面苯丙氨酸、甲硫氨酸和天冬酰胺诱导Ca-P涂层耐蚀性能比较[J]. 金属学报, 2021, 57(10): 1258-1271. [5] 陈永君, 白妍, 董闯, 解志文, 燕峰, 吴迪. 基于有限元分析的准晶磨料强化不锈钢表面钝化行为[J]. 金属学报, 2020, 56(6): 909-918. [6] 魏琳,王志军,吴庆峰,尚旭亮,李俊杰,王锦程. Mo元素及热处理对Ni2CrFeMox高熵合金在NaCl溶液中耐蚀性能的影响[J]. 金属学报, 2019, 55(7): 840-848. [7] 梁秀兵, 范建文, 张志彬, 陈永雄. 铝基非晶纳米晶复合涂层显微组织与腐蚀性能研究[J]. 金属学报, 2018, 54(8): 1193-1203. [8] 范丽, 陈海龑, 董耀华, 李雪莹, 董丽华, 尹衍升. 激光熔覆铁基合金涂层在HCl溶液中的腐蚀行为[J]. 金属学报, 2018, 54(7): 1019-1030. [9] 杨海欧, 尚旭亮, 王理林, 王志军, 王锦程, 林鑫. 单相CoCrFeNi高熵合金的组成元素对其在NaCl溶液中的耐蚀性能的影响[J]. 金属学报, 2018, 54(6): 905-910. [10] 杨柯, 牛梦超, 田家龙, 王威. 新一代飞机起落架用马氏体时效不锈钢的研究[J]. 金属学报, 2018, 54(11): 1567-1585. [11] 张二林, 王晓燕, 憨勇. 医用多孔Ti及钛合金的国内研究现状[J]. 金属学报, 2017, 53(12): 1555-1567. [12] 彭聪, 张书源, 任玲, 杨柯. 冷却速率对含Cu钛合金显微组织和性能的影响[J]. 金属学报, 2017, 53(10): 1377-1384. [13] 李慕勤, 姚海涛, 魏方红, 刘明达, 王赞, 彭书浩. 医用纯Mg表面多种复合处理膜层的组织结构和体内外性能[J]. 金属学报, 2017, 53(10): 1337-1346. [14] 田家龙,李永灿,王威,严伟,单以银,姜周华,杨柯. 多相强化型马氏体时效不锈钢中的合金元素偏聚效应*[J]. 金属学报, 2016, 52(12): 1517-1526. [15] 贺宏, 李静媛, 秦丽雁, 王一德, 房菲. 不同变形工艺后0Cr32Ni7Mo4N双相不锈钢的组织及性能*[J]. 金属学报, 2014, 50(1): 1-10. Viewed Full text Abstract Cited   Shared      Discussed