电磁场下近液相线高温合金熔体处理非枝晶组织的形成
高中堂, 胡锐(), 王军, 杨劼人, 李金山
西北工业大学凝固技术国家重点实验室, 西安 710072
EFFECT OF ELECTROMAGNETIC MELT TREATMENT NEAR LIQUIDUS ON THE FORMATION OF NON-DENDRITE MICROSTRUCTURE OF SUPERALLOY
GAO Zhongtang, HU Rui(), WANG Jun, YANG Jieren, LI Jinshan
State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072
引用本文:

高中堂, 胡锐, 王军, 杨劼人, 李金山. 电磁场下近液相线高温合金熔体处理非枝晶组织的形成[J]. 金属学报, 2014, 50(12): 1471-1477.
Zhongtang GAO, Rui HU, Jun WANG, Jieren YANG, Jinshan LI. EFFECT OF ELECTROMAGNETIC MELT TREATMENT NEAR LIQUIDUS ON THE FORMATION OF NON-DENDRITE MICROSTRUCTURE OF SUPERALLOY[J]. Acta Metall Sin, 2014, 50(12): 1471-1477.

全文: PDF(4190 KB)   HTML
摘要: 

采用电磁场近液相线熔体保温工艺对Ni-20Cr-18W (质量分数, %)高温合金进行处理, 获得了平均晶粒尺寸d=127 μm, 凝固组织为球状晶粒的60 kg铸锭. 借助于OM, SEM和EBSD等手段, 针对所获得的电磁场对原子团簇、界面稳定化以及树枝晶向球状晶转变的研究结果, 从形核热力学方面对近液相线处理后高温合金铸锭晶粒细化机制进行了研究. 结果表明: 该工艺能够细化凝固组织; 其细化机制为原子团簇与球晶分别作为后续凝固过程中的形核核心, 促进凝固过程中晶粒形核, 细化组织. 此外, 在改善熔体宏观温度场均匀性的基础上, 电磁场促进了球晶稳定化以及树枝晶向球状晶的转变, 并提高其形核率.

关键词 电磁场近液相线非枝晶组织形核率晶粒细化    
Abstract

The effects of electromagnetic field and melt treatment near liquidus on the grain refinement of the Ni-20Cr-18W (mass fraction, %) superalloy have been studied. The average grain size of 60 kg ingot can be refined to 127 μm and the grains are both ?ne and globular. Based on the effect of electromagnetic field on atomic cluster, interface stability and transformation from dendritic grain to globular grain, the mechanism of grain refinement has been studied from the aspect of nucleation thermodynamics by OM, SEM, EBSD. The results show that electromagnetic melt treatment near liquidus results in signi?cant re?nement. The grain refinement can be attributed to the mechanism that atomic clusters and globular structures can become the nucleus when the initial undercooling reaches certain level. Electromagnetic field not only improves homogeneity of the macroscopic temperature field, but also plays a positive role in interface stability and dendritic to globular transformation, which increases the nucleation rate.

Key wordselectromagnetic field    near liquidus    non-dendrite microstructure    nucleation rate    grain refinement
    
ZTFLH:  TG 211  
基金资助:*国家重点基础研究发展计划项目 2011CB610404, 高等学校学科创新引智计划项目 B08040和凝固技术国家重点实验室基金自主开放课题项目62-TP-2011资助
作者简介: null

高中堂, 男, 1983年生, 博士生

图1  60 kg Ni-20Cr-18W高温合金细晶铸锭EBSD和SEM分析取样示意图以及对应组织
图2  Ni-20Cr-18W高温合金不同区域EBSD像
图3  60 kg熔体取样示意图及其在2500 Hz, 17.6×106 A/m2条件下熔体温度分布
图4  Ni-20Cr-18W高温合金不同温度保温后的光学显微组织
图5  枝晶状组织固/液界面处Peltier热电效应示意图
图6  原子团簇与细小球状晶粒相互作用示意图
[1] Kotadia H R, Zhang H, Fan Z. Mater Lett, 2010; 64: 671
[2] Haghayehi R, Nastac L. Mater Lett, 2011; 65: 3230
[3] Xiong Y H, Li P J, Yang A M, Yan W D, Zeng D B, Liu L. Acta Metall Sin, 2002; 38: 529
[3] (熊玉华, 李培杰, 杨爱民, 严卫东, 曾大本, 刘 林. 金属学报, 2002; 38: 529)
[4] Zhou Y H. Solidification Technology. Beijing: Mechanical Industry Press, 1998: 55
[4] (周尧和. 凝固技术. 北京: 机械出版社, 1998: 55)
[5] Xia K, Tausing G. Mater Sci Eng, 1998; A246: 1
[6] Li X F, Zhang F, Zu F Q, Lv X, Zhao Z X, Yang D D. J Alloys Compd, 2010; 505: 472
[7] Wang Y Q, Wu Y Q, Liu J T, Bian X F. Chin Phy Lett, 2006; 23: 2513
[8] Men H, Jiang B, Fan Z. Acta Mater, 2010; 58: 6526
[9] Alirezar K, Miwa K J, Toshiyuki K S. Trans Nonferrous Met Soc China, 1998; 29: 1477
[10] Du Y Y, Lu Y P, Wang T M, Li T J, Zhang G L. Proc Eng, 2012; 27: 1129
[11] Wang J S, Xue Q G, Chang G W, Tang Y, Wang J Z, Cang D Q. J Univ Sci Technol Beijing, 2004; 11: 123
[12] Haghayeghi R, Nastac L. Mater Lett, 2011; 65: 3230
[13] Zhang X L, Li T J, Teng H T, Me S S, Jin J Z. Mater Sci Eng, 2007; A475: 194
[14] Wannasin J, Canyook R, Wisutmethangoon S, Flemings M C. Acta Mater, 2013; 61: 3897
[15] Li Q S, Song C J, Li H B, Zhai Q J. Mater Sci Eng, 2007; A466: 101
[16] Zi B T, Ba Q X, Cui J Z, Xu G M. Scr Mater, 2000; 43: 377
[17] He S X, Wang J, Zhou Y H. Acta Metall Sin, 2002; 38: 379
[17] (何树先, 王 俊, 周尧和. 金属学报, 2002; 38: 379)
[18] Liu Y, Hu R, Li J S. Mater Sci Eng, 2009; A508: 141
[19] Yue J T, Voltmer W. J Cryst Growth, 1975; 29: 32
[20] Li M J, Takuya T, Naoki O, Kenji M W. J Alloys Compd, 2009; 487: 187
[21] Shibayan R, Satyam S, Tamirisa K. Acta Mater, 2011; 59: 5494
[22] Zuo Y B, Cui J Z, Zhao H T. J Mater Sci, 2012; 47: 5501
[23] Wang B, Yang Y S, Zhou J X, Tong W H. Rare Met Mater Eng, 2009; 38: 519
[23] (汪 彬, 杨院生, 周吉学, 童文辉. 稀有金属材料与工程, 2009; 38: 519)
[24] Jia P, Wang E G, Lu L, He J C. Acta Metall Sin, 2013; 49: 1573
[24] (贾 鹏, 王恩刚, 鲁 辉, 赫冀成. 金属学报, 2013; 49: 1573)
[25] Fan Z, Wang Y, Xia M, Arumuganathar S. Acta Mater, 2009; 57: 4891
[26] Li T, Lin X, Huang W D. Acta Mater, 2006; 54: 4815
[27] Lin X, Tong L L, Zhao L N, Wanng L L, Wang M, Huang W D. Trans Nonferrous Met Soc China, 2010; 20: S826
[28] Dong J, Lu G M, Ren Q F, Cui J Z. Acta Metall Sin, 2002; 38: 203
[28] (董 杰, 路贵民, 任栖峰, 崔建中. 金属学报, 2002; 38: 203)
[29] Flemings M C. Solidification Processing. New York: McGraw Hill Book Company, 1974: 42
[30] Huang Y, Liu S, Lu D Y, Zhou Y H, Cheng G S, Zhang F S. Chin Space Sci Technol, 1989; 9(1): 7
[30] (黄 焰, 刘 山, 鲁德洋, 周尧和, 程功善, 张福生. 中国空间科学技术, 1989; 9(1): 7)
[31] Shu D, Sun B D, Mi J, Gran P S. Acta Mater, 2011; 59: 2
[1] 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎. W含量对Ti-42Al-5Mn-xW合金相转变行为的影响[J]. 金属学报, 2023, 59(10): 1401-1410.
[2] 吴国华, 童鑫, 蒋锐, 丁文江. 铸造Mg-RE合金晶粒细化行为研究现状与展望[J]. 金属学报, 2022, 58(4): 385-399.
[3] 丁宁, 王云峰, 刘轲, 朱训明, 李淑波, 杜文博. 高应变速率多向锻造Mg-8Gd-1Er-0.5Zr合金的微观组织、织构及力学性能[J]. 金属学报, 2021, 57(8): 1000-1008.
[4] 唐海燕, 刘锦文, 王凯民, 肖红, 李爱武, 张家泉. 连铸中间包加热技术及其冶金功能研究进展[J]. 金属学报, 2021, 57(10): 1229-1245.
[5] 任忠鸣,雷作胜,李传军,玄伟东,钟云波,李喜. 电磁冶金技术研究新进展[J]. 金属学报, 2020, 56(4): 583-600.
[6] 李秀程,孙明煜,赵靖霄,王学林,尚成嘉. 铁素体-贝氏体/马氏体双相钢中界面的定量化晶体学表征[J]. 金属学报, 2020, 56(4): 653-660.
[7] 武华健, 程仁山, 李景仁, 谢东升, 宋锴, 潘虎成, 秦高梧. Al含量对Mg-Sn-Ca合金微观组织与力学性能的影响[J]. 金属学报, 2020, 56(10): 1423-1432.
[8] 张军,介子奇,黄太文,杨文超,刘林,傅恒志. 镍基铸造高温合金等轴晶凝固成形技术的研究和进展[J]. 金属学报, 2019, 55(9): 1145-1159.
[9] 邓丽萍,崔凯旋,汪炳叔,向红亮,李强. AZ31镁合金室温多道次压缩过程微观组织和织构演变的研究[J]. 金属学报, 2019, 55(8): 976-986.
[10] 陶然, 赵玉涛, 陈刚, 怯喜周. 电磁场下原位合成纳米ZrB2 np/AA6111复合材料组织与性能研究[J]. 金属学报, 2019, 55(1): 160-170.
[11] 李淑波, 杜文博, 王旭东, 刘轲, 王朝辉. Zr对Mg-Gd-Er合金晶粒细化机理的影响[J]. 金属学报, 2018, 54(6): 911-917.
[12] 龚永勇, 程书敏, 钟玉义, 张云虎, 翟启杰. 脉冲磁致振荡凝固技术[J]. 金属学报, 2018, 54(5): 757-765.
[13] 王强, 何明, 朱晓伟, 李显亮, 吴春雷, 董书琳, 刘铁. 电磁场技术在冶金领域应用的数值模拟研究进展[J]. 金属学报, 2018, 54(2): 228-246.
[14] 毛轶哲, 李建国, 封蕾. 573 K高温时效处理的Al-10Mg合金中粗大β(Al3Mg2)相对热压缩组织演化的影响及机理[J]. 金属学报, 2018, 54(10): 1451-1460.
[15] 张丽丽, 江鸿翔, 赵九洲, 李璐, 孙倩. 溶质Ti对Al-Ti-B中间合金细化Al影响的新认识:TiB2粒子的动力学行为及溶质Ti的影响[J]. 金属学报, 2017, 53(9): 1091-1100.