一种高硼定向凝固合金的初熔行为及其对力学性能的影响
张洪伟1,2,秦学智2,李小武1,周兰章2(
)
)
Incipient Melting Behavior and Its Influences on the Mechanical Properties of a Directionally Solidified Ni-Based Superalloy with High Boron Content
Hongwei ZHANG1,2,Xuezhi QIN2,Xiaowu LI1,Lanzhang ZHOU2()
)
图8. 不同固溶处理后初熔区的SEM像(使用的腐蚀液为电解液A)
Fig.8. SEM images of IMR in the specimens solution treated at 1210 ℃ (a), 1230 ℃ (b) and 1250 ℃ (c) for 2 h and then followed by AC (Specimens were etched with electrolyte A)