图11. 锻态Z3CN20-09M双相不锈钢中铁素体的EBSD像
Fig.11. EBSD image of ferrite in Z3CN20-09M duplex stainless steel after 20% hot forged reduction+solution treatment at 1050 ℃ for 1 h