复合添加Y和Nd对Mg-Li合金显微组织及室温压缩织构的影响 |
崔崇亮,朱天龙,冷哲,巫瑞智,张景怀,张密林 |
哈尔滨工程大学材料科学与化学工程学院, 超轻材料与表面技术教育部重点实验室,哈尔滨 150001 |
|
EFFECTS OF COMBINED ADDITION OF Y AND Nd ON MICROSTRUCTURE AND TEXTURE AFTER COMPRESSION OF Mg-Li ALLOY AT ROOM TEMPERATURE |
CUI Chongliang,ZHU Tianlong,LENG Zhe,WU Ruizhi,ZHANG Jinghuai,ZHANG Milin |
Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 |
引用本文:
崔崇亮,朱天龙,冷哲,巫瑞智,张景怀,张密林. 复合添加Y和Nd对Mg-Li合金显微组织及室温压缩织构的影响[J]. 金属学报, 2012, 48(6): 725-732.
,
,
,
,
.
EFFECTS OF COMBINED ADDITION OF Y AND Nd ON MICROSTRUCTURE AND TEXTURE AFTER COMPRESSION OF Mg-Li ALLOY AT ROOM TEMPERATURE[J]. Acta Metall Sin, 2012, 48(6): 725-732.
[1] Wu R Z, Qu Z K, Zhang M L. Rev Adv Mater Sci, 2010; 24: 14[2] Liang C P, Gong H R. J Alloys Compd, 2010; 489: 130[3] Sasaki T T, Yamamoto K, Honma T. Scr Mater, 2008; 59: 1111[4] Wang T, Zhang M L, Niu Z Y, Liu B. J Rare Earths, 2006; 24: 797[5] Zhang M L, Meng X R, Wu R Z, Cui C L, Wu L B. Kovove Mater,2010; 211: 216[6] Liu X H, G J Du, R Z Wu, Z Y Niu, M L Zhang. J Alloys Compd,2011; 509: 9558[7] Li J Q, Qu Z K, Wu R Z, Zhang M L. Mater Sci Eng, 2011; A528: 3915[8] Wu L B, Cui C L, Wu R Z, Zhang M L. Mater Sci Eng, 2011; A528: 2174[9] Drozd Z, Trojanova Z, Kudela S. J Alloys Compd, 2004; 378: 192[10] Mishra R K, Gupta A K, Rao P R, Sachdev A K, Kumar A M, Luo A A. Scr Mater, 2008; 59: 562[11] Luo J R, Liu Q, Liu W, Godfrey A. Acta Metall Sin, 2011; 12: 1567 (罗晋如, 刘庆, 刘伟, Godfrey Andrew. 金属学报, 2011; 12: 1567)[12] Liu T, Zhang W, Wu S D. Mater Sci Eng, 2003; A360: 345[13] Li L, Zhou T T, Li H X, Chen C Q, Wu Q L, Zhang Q Q. Mater Sci Forum, 2007; 546-549: 347[14] Xiang Q, Wu R Z, Zhang M L. J Alloys Compd, 2009; 477: 832[15] Mukai T, Yamanoi M, Watanabe H. Scr Mater, 2001; 45: 89[16] Meng X R, Wu R Z, Zhang M L, Wu L B, Cui C L. J Alloys Compd,2009; 486: 722[17] Ando S, Tonda H. Mater Sci Forum, 2000; 350: 43[18] Agnew S R, Yoo M H, Tome C N. Acta Metall, 2001; 49: 4277[19] Stanford N, Atwell D, Barnett M R. Acta Metall, 2010; 58: 6773[20] Liu T, Wang Y D, Wu S D. Scr Mater, 2004; 51: 1057[21] Dong H W, Wang L D, Wu Y M, Wang L M. J Alloys Compd,2010; 506: 468[22] Takuda H, Kikuchi S, Yoshida N, Okahara H. Mater Trans,2003; 44: 2266[23] Song Y, Shan D, Chen R, Han E H. Corros Sci, 2009; 51: 1087[24] Wei S Q, Zhang M L, Han W, Yan Y D, Zhang B. Acta Metall Sin,2011; 47: 173 (魏树权, 张密林, 韩伟, 颜永得, 张斌. 金属学报, 2011; 47: 173)[25] Ye K, Chen Y, Zhang M L, Han W, Yan Y D, Wei S Q. Chem Lett,2010; 28: 128[26] Bohlen J, Yi S, Letzig D, Kainer K U. Mater Sci Eng,2010; A527: 7092[27] Hantzsche K, Bohlen J, Wendt J, Kainer K U, Yi S B,Letzig D. Scr Mater, 2010; 63: 725[28] Cui C L, Wu L B, Wu R Z, Zhang J H, Zhang M L. J Alloys Compd, 2011; 509: 9045[29] Koike J. Mater Sci Forum, 2003; 189: 419[30] Li T Q, Liu Y B, Cao Z Y, Wu R Z, Zhang M L, Cheng L R,Jiang D M. J Alloys Compd, 2011; 509: 7607[31] Guo X T, Liu P J, Zeng D B. J Chin Rare Earths, 2003; 21: 672 (郭旭涛, 李培杰, 曾大本. 中国稀土学报, 2003; 21: 672)[32] Chino Y, Kado M, Mabuchi M. Mater Sci Eng, 2008; A494: 343[33] Li Z J, Jin Q L, Jiang Y H, Zhou R. Acta Metall Sin, 2009; 45: 924 (李再久, 金青林, 蒋业华, 周荣. 金属学报, 2009; 45: 924) |
|