金属学报  1993, Vol. 29 Issue (10): 46-50

论文 本期目录 | 过刊浏览 |

液态模锻钢平法兰裂纹扩展的研究

罗守靖;胡连喜;霍文灿

哈尔滨工业大学;哈尔滨工业大学;哈尔滨工业大学

GROWTH OF HOT CRACKS IN LIQUID-FORGED STEEL FLAT FLANGES

LUO Shoujing;HU Lianxi;HUO Wencan Harbin Institute of Technology

罗守靖;胡连喜;霍文灿. 液态模锻钢平法兰裂纹扩展的研究[J]. 金属学报, 1993, 29(10): 46-50.
, , . GROWTH OF HOT CRACKS IN LIQUID-FORGED STEEL FLAT FLANGES[J]. Acta Metall Sin, 1993, 29(10): 46-50.

摘要 参考文献 相关文章 Metrics 全文: PDF(1757 KB)   摘要: 观察和分析了液态模锻钢平法兰热裂纹的形貌与组织特征.发现裂纹一旦形成,其扩展经历四个阶段,表现为裂纹开展面上具有四个明显的特征区、裂纹的扩展程度与钢液质量、凝固条件及制件受力状态等工艺因素有关 关键词 ： 液态模锻,  钢平法兰,  热裂纹     Abstract：The morphology and feature of hot cracks in liquid forged steel flat frangeshave been observed. Once the cracks occur, they will propagate throguh 4 stages, and revealthemselves obviously as 4 featured zones. The growth of the hot cracks seems to be depen-dent upon certain technological factors, such as: liquid steel quality, solidification and stressedstate on workpieces, etc. Key words： liquid forging    steel flat flange    hot crack 收稿日期: 1993-10-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 罗守靖 胡连喜 霍文灿 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1993/V29/I10/46 1． 孙宗玉,罗守靖,彭其凤.山东机械,1984;(3) :13 2． 罗守靖,霍文灿,胡连喜.钢铁,1991;(8) :54 [1] 卢楠楠, 郭以沫, 杨树林, 梁静静, 周亦胄, 孙晓峰, 李金国. 激光增材修复单晶高温合金的热裂纹形成机制[J]. 金属学报, 2023, 59(9): 1243-1252. [2] 王学, 李勇, 王家庆, 胡磊. 高温时效对T23钢粗晶热影响区显微组织及再热裂纹敏感性的影响[J]. 金属学报, 2021, 57(6): 736-748. [3] 邵盈恺, 王玉玺, 杨志斌, 史春元. 基于焊缝熔深优化的7075铝合金等离子-MIG复合焊接热裂纹敏感性[J]. 金属学报, 2018, 54(4): 547-556. [4] 温鹏 荻崎贤二 山本元道. 激光焊接过程中残留液体金属的高速高倍在线观察[J]. 金属学报, 2011, 47(3): 305-310. [5] 温鹏 荻崎贤二 山本元道. 环形结构激光焊接凝固热裂纹的实验研究和数值模拟[J]. 金属学报, 2011, 47(10): 1241-1245. [6] 郑贤淑;金俊泽. 电磁铸造大板坯凝固过程中热裂纹萌生机理分析[J]. 金属学报, 1995, 31(23): 511-517. Viewed Full text Abstract Cited   Shared      Discussed