2205钢在模拟深海热液区中的腐蚀行为 |
屈少鹏1(), 程柏璋1, 董丽华1, 尹衍升1, 杨丽景2 |
1 上海海事大学海洋科学与工程学院 上海 201306 2 中国科学院宁波材料技术与工程研究所中国科学院海洋新材料与应用技术重点实验室 宁波 315201 |
|
Corrosion Behavior of 2205 Steel in Simulated Hydrothermal Area |
Shaopeng QU1(), Baizhang CHENG1, Lihua DONG1, Yansheng YIN1, Lijing YANG2 |
1 College of Ocean Science and Engineering, Shanghai Maritime University, Shanghai 201306, China 2 Key Laboratory of Marine Materials and Related Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China |
引用本文:
屈少鹏, 程柏璋, 董丽华, 尹衍升, 杨丽景. 2205钢在模拟深海热液区中的腐蚀行为[J]. 金属学报, 2018, 54(8): 1094-1104.
Shaopeng QU,
Baizhang CHENG,
Lihua DONG,
Yansheng YIN,
Lijing YANG.
Corrosion Behavior of 2205 Steel in Simulated Hydrothermal Area[J]. Acta Metall Sin, 2018, 54(8): 1094-1104.
[1] | Spiess F N, Macdonald K C, Atwater T, et al.East pacific rise: Hot springs and geophysical experiments[J]. Science, 1980, 207: 1421 | [2] | Haymon R M, Macdonald K C.The geology of deep-sea hot springs[J]. Am. Sci., 1985, 73: 441 | [3] | Feng J, Li J H, Chen Z, et al.A review on "black smokers" and its implication for origin of life[J]. Acta Sci. Nat. Univ. Peking, 2004, 40: 318(冯军, 李江海, 陈征等. “海底黑烟囱”与生命起源述评[J]. 北京大学学报(自然科学版), 2004, 40: 318) | [4] | Zeng Z G, Liu C H, Yin X B, et al.Initial findings of first global voyage of Dayang No. 1 (DY105-17A) in East Pacific Rise[J]. Acta Mineral. Sin., 2007, 27(suppl.): 369(曾志刚, 刘长华, 殷学博等. 大洋一号首次环球航次(DY105-17A)在东太平洋海隆的初步调查结果[J]. 矿物学报, 2007, 27(增刊): 369) | [5] | Wu Z W, Sun X M, Dai Y Z, et al.The discovery of native gold in massive sulfidesfrom the Edmond hydrothermal field, Central Indian Ridge and its significance[J]. Acta Petrol. Sin., 2011, 27: 3749(吴仲玮, 孙晓明, 戴瑛知等. 中印度洋海岭Edmond热液区块状硫化物中自然金的发现及其意义[J]. 岩石学报, 2011, 27: 3749) | [6] | Guo J J, Yu Z H, Li H M.Rare earth elements in the sediments from Baoshishan hydrothermal field near the Galapagos microplate[J]. Period. Ocean Univ. China, 2013, 43(12): 66(郭静静, 于增慧, 李怀明. Galapagos微板块附近宝石山热液区沉积物稀土元素组成特征[J]. 中国海洋大学学报, 2013, 43(12): 66) | [7] | Zhang Y.Study on welding structure stress corrosion fatigue properties of 2205 duplex stainless steel [D]. Chongqing: Chongqing Jiaotong University, 2013(张瑶. 2205双相不锈钢焊接结构应力腐蚀疲劳性能研究 [D]. 重庆: 重庆交通大学, 2013) | [8] | Fan Q Q, Hua L.Influence factor of corrosion behavior of 2205 duplex stainless steel[J]. Corros. Sci. Prot. Technol., 2014, 26: 178(范强强, 华丽. 2205双相不锈钢腐蚀行为的影响因素[J]. 腐蚀科学与防护技术, 2014, 26: 178) | [9] | Feng H, Zhou X Y, Liu H, et al.Development and trend of hyper duplex stainless steels[J]. J. Iron Steel Res., 2015, 27(4): 1(丰涵, 周晓玉, 刘虎等. 特超级双相不锈钢的发展现状及趋势[J]. 钢铁研究学报, 2015, 27(4): 1) | [10] | Cheng B Z, Qu S P, Dong L H, et al. The influence of hydrostatic pressure on the corrosion electrochemistry characters of2205 steel in deep sea environment[J]. Corros. Prot., 2018, 39: doi: 10.11973/fsyfh-201811001(程柏璋, 屈少鹏, 董丽华等. 深海环境中静水压对2205钢腐蚀电化学性质的影响 [J]. 腐蚀与防护, 2018, 39: doi: 10.11973/fsyfh-201811001) | [11] | Xu Y S, Xie H S, Guo J, et al.Conductivity of NaCl solution at 0.4-5.0 GPa and 25-500 ℃[J]. Sci. China, 1997, 27D: 398(徐有生, 谢鸿森, 郭捷等. 0.4~5.0 GPa和室温~500 ℃下NaCl溶液的电导率[J]. 中国科学, 1997, 27D: 133) | [12] | Cao C N.On the theoretical errors of linear polarization techniques[J]. J. Chin. Soc. Corros. Prot., 1981, 1(2): 1(曹楚南. 线性极化电阻的理论误差及其纠正方法[J]. 中国腐蚀与防护学报, 1981, 1(2): 1) | [13] | Wang F P, Jing H M, Xin C M.Electrochemistry of Corrosion [M]. 2nd Ed., Beijing: Chemical Industry Press, 2017: 199(王凤平, 敬和民, 辛春梅. 腐蚀电化学 [M]. 第2版, 北京: 化学工业出版社, 2017: 199) | [14] | Cao C N.Principles of Electrochemistry of Corrosion [M]. 3rd Ed., Beijing: Chemical Industry Press, 2008: 127(曹楚南. 腐蚀电化学原理 [M]. 第3版, 北京: 化学工业出版社, 2008: 127) | [15] | Han D, Jiang Y M, Deng B, et al.Effect of aging time on electrochemical corrosion behavior of 2101 duplex stainless steel[J]. Acta Metall. Sin., 2009, 45: 919(韩冬, 蒋益明, 邓博等. 时效时间对2101双相不锈钢电化学腐蚀行为的影响[J]. 金属学报, 2009, 45: 919) | [16] | Dong C F, Xiao K, Chen T, et al.Characterization and comparison of conducting polyaniline synthesized by three different pathways[J]. J. Wuhan Univ. Technol.-Mater. Sci. Ed., 2011, 26: 1068 | [17] | Du N, Tian W M, Zhao Q, et al.Pitting corrosion dynamics and mechanisms of 304 stainless steel in 3.5%NaCl solution[J]. Acta Metall. Sin., 2012, 48: 807(杜楠, 田文明, 赵晴等. 304不锈钢在3.5%NaCl溶液中的点蚀动力学及机理[J]. 金属学报, 2012, 48: 807) | [18] | Schultze J W, Lohrengel M M.Stability, reactivity and breakdown of passive films. Problems of recent and future research[J]. Electrochim. Acta, 2000, 45: 2499 | [19] | Sikora E, Macdonald D D.Nature of the passive film on nickel[J]. Electrochim. Acta, 2002, 48: 69 | [20] | Cai W T, Zhao G X, Zhao D W, et al.Corrosion resistance and semiconductor properties of passive films formed on super 13Cr stainless steel[J]. J. Univ. Sci. Technol. Beijing, 2011, 33: 1226(蔡文婷, 赵国仙, 赵大伟等. 超级13Cr不锈钢的钝化膜耐蚀性与半导体特性[J]. 北京科技大学学报, 2011, 33: 1226) | [21] | Kim J S, Cho E A, Kwon H S.Photoelectrochemical study on the passive film on Fe[J]. Corros. Sci., 2001, 43: 1403 | [22] | Zhang C X, Zhang Z H.Corrosion resistance of the passive films formed on the G3 nickel-base alloy in different conditions[J]. Baosteel Technol., 2008, 26(5): 35(张春霞, 张忠铧. G3镍基合金钝化膜的耐蚀性研究[J]. 宝钢技术, 2008, 26(5): 35) | [23] | Wang C, Zhi Y M, Sheng M Q, et al.Semiconductor characters of passive film on AISI304 stainless steel surface in electrolytes during corrosion process[J]. Corros. Prot., 2009, 30: 369(王超, 支玉明, 盛敏奇等. AISI304不锈钢钝化膜在电解质溶液中腐蚀时的半导体性质[J]. 腐蚀与防护, 2009, 30: 369) | [24] | Melchers R E.Pitting corrosion of mild steel in marine immersion environment-Part 2: Variability of maximum pit depth[J]. Corrosion, 2004, 60: 937 | [25] | Wang B C, Zhu J H.Semiconducting behaviors of passive films of stainless steel under ultrasonic cavitation[J]. Acta Metall. Sin., 2007, 43: 813(王保成, 朱金华. 超声空化下不锈钢钝化膜的半导行为[J]. 金属学报, 2007, 43: 813) | [26] | Macdonald D D.The point defect model for the passive state[J]. J. Electrochem. Soc., 1992, 139: 3434 | [27] | Gao L, Wang B C.Influence of corrosion behaviors and semiconductor properties for passive film of SUS304 and SUS430 stainless steel by temperature[J]. J. Taiyuan Univ. Technol., 2015, 46: 268(高磊, 王保成. 温度对SUS304与SUS430不锈钢耐腐蚀性及其钝化膜半导体性能的影响[J]. 太原理工大学学报, 2015, 46: 268) | [28] | Shu J.Investigation on corrosion resistance properties and formabilities of ferritic stainless steel used as aumotive exhaust system [D]. Shanghai: Shanghai Jiao Tong University, 2013(舒俊. 汽车排气系统用铁素体不锈钢耐蚀性能和成形性能的研究 [D]. 上海: 上海交通大学, 2013) |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|