电磁复合场对Ni60合金凝固过程中显微组织和裂纹的影响
林英华1,2, 袁莹1,2, 王梁1,2, 胡勇1,2, 张群莉1,2, 姚建华1,2()
1 浙江工业大学激光先进制造研究院 杭州 310014
2 浙江省高端激光制造装备协同创新中心 杭州 310014
Effect of Electric-Magnetic Compound Field on the Microstructure and Crack in Solidified Ni60 Alloy
Yinghua LIN1,2, Ying YUAN1,2, Liang WANG1,2, Yong HU1,2, Qunli ZHANG1,2, Jianhua YAO1,2()
1 Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou 310014, China
2 Zhejiang Provincial Collaborative Innovation Center of High-End Laser Manufacturing Equipment, Hangzhou 310014, China
引用本文:

林英华, 袁莹, 王梁, 胡勇, 张群莉, 姚建华. 电磁复合场对Ni60合金凝固过程中显微组织和裂纹的影响[J]. 金属学报, 2018, 54(10): 1442-1450.
Yinghua LIN, Ying YUAN, Liang WANG, Yong HU, Qunli ZHANG, Jianhua YAO. Effect of Electric-Magnetic Compound Field on the Microstructure and Crack in Solidified Ni60 Alloy[J]. Acta Metall Sin, 2018, 54(10): 1442-1450.

全文: PDF(5527 KB)   HTML
摘要: 

利用电磁复合场协同激光熔覆制备多道Ni60合金熔覆层,运用着色探伤剂、OM、SEM、EDS、XRD与硬度测试等实验手段,对制备的Ni60合金熔覆层进行测试分析。结果表明,施加电磁复合场之前,制备的Ni60合金熔覆层表面出现明显开裂,内部存在大尺寸气孔,表面成形质量差;施加电磁复合场之后,Ni60合金熔覆层表面裂纹得到了抑制,内部气孔消失,且熔覆层表面成形质量也得到了改善。同时,施加电磁复合场后,制备的Ni60合金熔覆层的脆性相(CrB和(Cr, Fe)23C6 )颗粒尺寸从4~6 μm降低至2~4 μm,且颗粒偏聚得到降低,并有效地消除了内部裂纹。施加电磁复合场之后,熔覆层内部的脆性相含量、颗粒偏聚、晶格畸变和硬度均减少,降低了裂纹萌生的几率,从而有效地抑制了内部裂纹的形成。

关键词 Ni60合金激光熔覆电磁复合场裂纹    
Abstract

Ni60 alloy has been widely used in many application fields due to its excellent wear resistance, corrosion resistance and high temperature oxidation resistance. However, uneven microstructure was easily formed due to the effect of heat shock and heat accumulation during laser multi-track overlap process. Moreover, Ni60 alloy powder was composed of a variety of elements. The composition segregation and high content CrB, (Cr, Fe)23C6 were easily present in the coating during the laser cladding process, which can easily lead to the cracking of Ni60 alloy coating. In this work, multi-layer Ni60 alloy coating was prepared by electric-magnetic compound field assisted laser cladding. Synthesis of Ni60 alloy coating was analyzed by coloring agent, OM, SEM, EDS, XRD and microhardness tester. The results showed that cracks and large pores were to appear at the coating when the electric-magnetic compound field was not applied, and the molding quality was also poor. When the electric-magnetic compound field was applied, the surface cracks of Ni60 alloy coating were suppressed, the pores were eliminated, and the molding quality of the coating was also improved. Meanwhile, the particle size of the brittle phase (CrB, (Cr, Fe)23C6) was decreased from 4~6 μm to 2~4 μm by the aid of the electric-magnetic compound field, and the degree of particle cluster was also reduced, which was beneficial to the elimination of the internal crack. XRD, microstructure and microhardness analysis results showed that the brittle phase content, particle segregation, lattice distortion and hardness were reduced under the condition of electric-magnetic compound field, leading to the decrease of crack initiation probability, so the crack of Ni60 alloy coating was remarkably reduced.

Key wordsNi60 alloy    laser cladding    electric-magnetic compound field    crack
收稿日期: 2018-04-11     
ZTFLH:  TN249  
基金资助:国家重点研发计划项目No.2017YFB1103601,国家自然科学基金项目No.51475429和中国博士后科学基金项目No.2017M610376
作者简介:

作者简介 林英华,男,1985年生,博士

图1  电磁复合场(EMCF)辅助激光熔覆过程示意图
图2  施加EMCF前后Ni60合金熔覆层的表面着色探伤图
图3  施加EMCF前后Ni60合金熔覆层纵截面OM像
图4  施加EMCF前后不同道次熔覆层厚度
图5  施加EMCF前后Ni60合金熔覆层表层和底部的XRD谱
图6  未施加EMCF的Ni60合金第1和第5道次熔覆层横截面的SEM像
图7  未施加EMCF的Ni60合金第2道次熔覆层内部裂纹和周围显微组织的SEM像
Position C Si Cr Fe Ni Mo
1 41.06 1.28 50.24 5.40 1.78 0.24
2 39.93 0.56 11.27 29.35 18.30 0.59
3 39.28 1.30 47.36 8.16 3.63 0.27
4 39.21 0.45 13.63 28.51 17.73 0.47
5 37.63 0.56 48.07 9.10 4.42 0.22
6 36.53 0.39 20.41 27.30 15.16 0.21
7 37.92 0.54 45.13 10.34 5.82 0.25
8 35.83 0.67 17.28 25.76 20.23 0.23
表1  图6和图8中不同位置的EDS分析结果
图8  施加EMCF后Ni60合金第1和第5道次熔覆层横截面的SEM像
图9  施加EMCF前后Ni60合金第1道次熔覆层横截面显微硬度
图10  施加EMCF前物相偏聚示意图
[1] Yao J H, Yang L J, Li B, et al.Beneficial effects of laser irradiation on the deposition process of diamond/Ni60 composite coating with cold spray[J]. Appl. Surf. Sci., 2015, 330: 300
[2] Wen Z H, Bai Y, Yang J F, et al.Effect of vacuum re-melting on the solid particles erosion behavior of Ni60-NiCrMoY composite coatings prepared by plasma spraying[J]. Vacuum, 2016, 134: 73
[3] Xu B S, Fang J X, Dong S Y, et al.Heat-affected zone microstructure evolution and its effects on mechanical properties for laser cladding FV520B stainless steel[J]. Acta Metall. Sin., 2015, 52: 1(徐滨士, 方金祥, 董世运等. FV520B不锈钢激光熔覆热影响区组织演变及其对力学性能的影响[J]. 金属学报, 2015, 52: 1)
[4] Ocelík V, Furár I, De Hosson J T M. Microstructure and properties of laser clad coatings studied by orientation imaging microscopy[J]. Acta Mater., 2010, 58: 6763
[5] Yao J H, Yang L J, Li B, et al.Characteristics and performance of hard Ni60 alloy coating produced with supersonic laser deposition technique[J]. Mater. Des., 2015, 83: 26
[6] Lu X L, Liu X B, Yu P C, et al.Synthesis and characterization of Ni60-hBN high temperature self-lubricating anti-wear composite coatings on Ti6Al4V alloy by laser cladding[J]. Opt. Laser Technol., 2016, 78: 87
[7] Ma Q S, Li Y J, Wang J, et al.Microstructure evolution and growth control of ceramic particles in wide-band laser clad Ni60/WC composite coatings[J]. Mater. Des., 2016, 92: 897
[8] Zhang J, Hu Y, Tan X J, et al.Microstructure and high temperature tribological behavior of laser cladding Ni60A alloys coatings on 45 steel substrate[J]. Trans. Nonferrous Met. Soc. China, 2015, 25: 1525
[9] Shu D, Li Z G, Zhang K, et al.In situ synthesized high volume fraction WC reinforced Ni-based coating by laser cladding[J]. Mater Lett., 2017, 195: 178
[10] Wang L, Yao J H, Hu Y, et al.Influence of electric-magnetic compound field on the WC particles distribution in laser melt injection[J]. Surf. Coat. Technol., 2017, 315: 32
[11] Wang L, Yao J H, Hu Y, et al.Suppression effect of a steady magnetic field on molten pool during laser remelting[J]. Appl. Surf. Sci., 2015, 351: 794
[12] Bachmann M, Avilov V, Gumenyuk A, et al.About the influence of a steady magnetic field on weld pool dynamics in partial penetration high power laser beam welding of thick aluminium parts[J]. Int. J. Heat. Mass. Transfer, 2013, 60: 309
[13] Rong Y M, Xu J J, Cao H Y, et al.Influence of steady magnetic field on dynamic behavior mechanism in full penetration laser beam welding[J]. J. Manuf. Process., 2017, 26: 399
[14] Chen J C, Wei Y H, Zhan X H, et al.Melt flow and thermal transfer during magnetically supported laser beam welding of thick aluminum alloy plates[J]. J. Mater. Process. Technol., 2018, 254: 325
[15] Wang L, Wu C S, Chen J, et al.Influence of the external magnetic field on fluid flow, temperature profile and humping bead in high speed gas metal arc welding[J]. Int. J. Heat Mass Transfer, 2018, 116: 1282
[16] Wen Z H, Bai Y, Yang J F, et al.Corrosion resistance of vacuum re-melted Ni60-NiCrMoY alloy coatings[J]. J. Alloys Compd., 2017, 711: 659
[17] Luo F, Cockburn A, Sparkes M, et al.Performance characterization of Ni60-WC coating on steel processed with supersonic laser deposition[J]. Defence Technol., 2015, 11: 35
[18] Chen G, Gao Z Y.Effect of welding processing parameters on porosity formation of mild steel treated by CO2 laser deep penetration welding[J]. Acta Metall. Sin., 2013, 49: 181(陈高, 高子英. 焊接工艺参数对低碳钢CO2激光深熔焊接气孔形成的影响[J]. 金属学报, 2013, 49: 181)
[19] Wei H L, Elmer J W, DebRoy T. Crystal growth during keyhole mode laser welding[J]. Acta Mater., 2017, 133: 10
[20] Chen M H, Xu J N, Xin L J, et al.Effect of keyhole characteristics on porosity formation during pulsed laser-GTA hybrid welding of AZ31B magnesium alloy[J]. Opt. Laser Eng., 2017, 93: 139
[21] Ma Q S, Li Y J, Wang J, et al.Investigation on cored-eutectic structure in Ni60/WC composite coatings fabricated by wide-band laser cladding[J]. J. Alloys Compd., 2015, 645: 151
[22] Cai Y C, Luo Z, Feng M N, et al.The effect of TiC/Al2O3 composite ceramic reinforcement on tribological behavior of laser cladding Ni60 alloys coatings[J]. Surf. Coat. Technol., 2016, 291: 222
[23] Wen P, Shinozaki K, Yamamoto M.Experimental research and numerical simulation of solidification crack during laser welding of ring structure[J]. Acta Metall. Sin., 2011, 47: 1241(温鹏, 荻崎贤二, 山本元道. 环形结构激光焊接凝固热裂纹的实验研究和数值模拟[J]. 金属学报, 2011, 47: 1241)
[24] Na S, Yoon D, Kim J, et al.An evaluation of the fatigue crack propagation rate for powder metallurgical nickel-based superalloys using the DCPD method at elevated temperatures[J]. Int. J. Fatigue., 2017, 101: 27
[25] Yan F, Liu S, Hu C J, et al.Liquation cracking behavior and control in the heat affected zone of GH909 alloy during Nd: YAG laser welding[J]. J. Mater. Process. Technol., 2017, 244: 44
[26] Ye X, Hua X M, Wang M, et al.Controlling hot cracking in Ni-based Inconel-718 superalloy cast sheets during tungsten inert gas welding[J]. J. Mater. Process. Technol., 2015, 222: 381
[1] 卢楠楠, 郭以沫, 杨树林, 梁静静, 周亦胄, 孙晓峰, 李金国. 激光增材修复单晶高温合金的热裂纹形成机制[J]. 金属学报, 2023, 59(9): 1243-1252.
[2] 江河, 佴启亮, 徐超, 赵晓, 姚志浩, 董建新. 镍基高温合金疲劳裂纹急速扩展敏感温度及成因[J]. 金属学报, 2023, 59(9): 1190-1200.
[3] 穆亚航, 张雪, 陈梓名, 孙晓峰, 梁静静, 李金国, 周亦胄. 基于热力学计算与机器学习的增材制造镍基高温合金裂纹敏感性预测模型[J]. 金属学报, 2023, 59(8): 1075-1086.
[4] 韩卫忠, 卢岩, 张雨衡. 体心立方金属韧脆转变机制研究进展[J]. 金属学报, 2023, 59(3): 335-348.
[5] 常立涛. 压水堆主回路高温水中奥氏体不锈钢加工表面的腐蚀与应力腐蚀裂纹萌生:研究进展及展望[J]. 金属学报, 2023, 59(2): 191-204.
[6] 杨杜, 白琴, 胡悦, 张勇, 李志军, 蒋力, 夏爽, 周邦新. GH3535合金中晶界特征对碲致脆性开裂影响的分形分析[J]. 金属学报, 2023, 59(2): 248-256.
[7] 戚钊, 王斌, 张鹏, 刘睿, 张振军, 张哲峰. 应力比对含缺陷选区激光熔化TC4合金稳态疲劳裂纹扩展速率的影响[J]. 金属学报, 2023, 59(10): 1411-1418.
[8] 彭治强, 柳前, 郭东伟, 曾子航, 曹江海, 侯自兵. 基于大数据挖掘的连铸结晶器传热独立变化规律[J]. 金属学报, 2023, 59(10): 1389-1400.
[9] 祝国梁, 孔德成, 周文哲, 贺戬, 董安平, 疏达, 孙宝德. 选区激光熔化 γ' 相强化镍基高温合金裂纹形成机理与抗裂纹设计研究进展[J]. 金属学报, 2023, 59(1): 16-30.
[10] 周红伟, 高建兵, 沈加明, 赵伟, 白凤梅, 何宜柱. 高温低周疲劳下C-HRA-5奥氏体耐热钢中孪晶界演变[J]. 金属学报, 2022, 58(8): 1013-1023.
[11] 杨秦政, 杨晓光, 黄渭清, 石多奇. 粉末高温合金FGH4096的疲劳小裂纹扩展行为[J]. 金属学报, 2022, 58(5): 683-694.
[12] 冯凯, 郭彦兵, 冯育磊, 姚成武, 朱彦彦, 张群莉, 李铸国. 激光熔覆高强韧铁基涂层精细组织调控与性能研究[J]. 金属学报, 2022, 58(4): 513-528.
[13] 李细锋, 李天乐, 安大勇, 吴会平, 陈劼实, 陈军. 钛合金及其扩散焊疲劳特性研究进展[J]. 金属学报, 2022, 58(4): 473-485.
[14] 余春, 徐济进, 魏啸, 陆皓. 核级镍基合金焊接材料失塑裂纹研究现状[J]. 金属学报, 2022, 58(4): 529-540.
[15] 郭昊函, 杨杰, 刘芳, 卢荣生. GH4169合金拘束相关的疲劳裂纹萌生寿命[J]. 金属学报, 2022, 58(12): 1633-1644.