7050铝合金淬火敏感性研究和微观组织分析*
吴书舟1,易幼平1,黄始全1(),李俊1,李晨2
1 中南大学机电工程学院高性能复杂制造国家重点实验室, 长沙 410083
2 中航工业第一飞机设计研究院, 西安 710089
RESERCH ON QUENCH SENSITIVITY AND MICROSTRUCTURE ANALYSIS OF 7050 ALUMINUM ALLOY
Shuzhou WU1,Youping YI1,Shiquan HUANG1(),Jun LI1,Chen LI2
1 State Key Laboratory of High Performance Complex Manufacturing, School of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China
2 The First Aircraft Institute of AVIC, Xi'an 710089, China
引用本文:

吴书舟,易幼平,黄始全,李俊,李晨. 7050铝合金淬火敏感性研究和微观组织分析*[J]. 金属学报, 2016, 52(12): 1503-1509.
Shuzhou WU, Youping YI, Shiquan HUANG, Jun LI, Chen LI. RESERCH ON QUENCH SENSITIVITY AND MICROSTRUCTURE ANALYSIS OF 7050 ALUMINUM ALLOY[J]. Acta Metall Sin, 2016, 52(12): 1503-1509.

全文: PDF(4956 KB)   HTML
摘要: 

通过分级淬火方法测定了7050铝合金的TTT曲线, 采用TEM和JMA方程等分析手段研究了固溶、等温淬火和时效过程中微观组织的演变规律及其动力学特性. 结果表明, 合金TTT曲线的鼻尖温度在330 ℃附近, 淬火敏感区间为300~380 ℃, 高温区(400~450 ℃)淬火敏感性低于低温区(210~270 ℃); 等温保温过程中过饱和固溶体主要析出以Al3Zr粒子为形核核心的片层状η平衡相及少量针状S相, 随保温时间延长析出相体积分数快速增加, 同时在晶界排列变得连续而粗化、无沉淀析出带(PFZ)宽化, 在远离鼻尖的温度下保温合金析出速率减慢, 在晶界排布连续化和粗化程度降低; JMA方程中反映析出相形态的常数n在0.50~0.65的范围内, 析出相特征以片层状相为主、针状相为辅.

关键词 7050铝合金,TTT曲线,淬火敏感性,相变动力学,微观组织    
Abstract

7050 aluminum alloy is an important structural material widely used in aerospace industry with a high quench sensitivity. In this work, the time-temperature-transformation (TTT) curves of 7050 aluminum alloy were determined by interrupted quench method. The microstructure evolution and phase transformation kinetics during solid solution, isothermal quenching, ageing treatment were studied by TEM and JMA equation.The results show that the nose temperature of TTT curves is about 330 ℃, with the quench sensitivity range of 300~380 ℃. The quenching sensitivity of high temperature range of 400~450 ℃ is lower than that of low temperature range of 210~270 ℃. The laminar equilibrium η phases characterized with nucleus of Al3Zr particles and several needle-shaped S phases are the main precipitations of the supersaturated solid solution decomposes during isothermal holding process. With the increase of holding time, the volume fraction of precipitated phases rises quickly, which coarsen the grain boundary continuously and broaden precipitation free zone (PFZ). While holding far away from the nose temperature, the speed of precipitation slow down and the degree of continuity and coarsening of grain boundary decrease. The values of n in JMA equation vary from 0.50 to 0.65, indicating that the precipitations are mainly laminar precipitated phases and supplementarily needle-shaped phases.

Key words7050    aluminum    alloy,    TTT    curve,    quench    sensitivity,    phase    transformation    kinetics,    microstructure
收稿日期: 2016-02-01     
基金资助:*国家重点基础研究发展计划项目2012CB619504, 国家国际科技合作专项项目2014DFA51250, 以及高性能复杂制造国家重点实验室项目zzyjkt2014-02资助
图1  7050铝合金锻件金相组织
图2  不同等温温度下等温时间对等温淬火态合金电导率的影响
图3  7050铝合金等温保温过程的时间-温度-转化率(TTT)曲线
Temperature / ℃ k n
250 0.012 0.632
270 0.021 0.617
300 0.028 0.635
315 0.036 0.617
330 0.056 0.536
360 0.041 0.534
380 0.025 0.551
400 0.018 0.533
420 0.010 0.567
表1  7050铝合金S曲线的拟合参数
图4  7050铝合金的等温转变S曲线
图5  330 ℃保温不同时间后淬火态合金的TEM像
图6  不同温度下保温300 s时效态合金的TEM像
[1] Wang Z T, Tian R Z.Aluminum Alloy and Processing Handbook. Changsha: Central South University of Technology Press, 1989: 34
[1] (王祝堂, 田荣璋. 铝合金及其加工手册. 长沙: 中南工业大学出版社, 1989: 34)
[2] Zhang X M, Deng Y L, Zhang Y.Acta Metall Sin, 2015; 51: 268
[2] (张新明, 邓运来, 张勇. 金属学报, 2015; 51: 268)
[3] Li C G, Wu S J, Dai S L.Trans Nonferrous Met Soc China, 2002; 12: 15
[3] (李成功, 巫世杰, 戴圣龙. 中国有色金属学报, 2002; 12: 15)
[4] Sampson D S, translated by Hong R X. Album of Deformation Aluminum Alloy in Modern Times. Beijing: Metallurgy Industry Press, 1987: 97
[4] (Sampson D S 著, 洪仁先译. 国外近代变形铝合金专集. 北京: 冶金工业出版社, 1987: 97)
[5] Liu Y Z, Li Z L, Gu C X.Acta Metall Sin, 2013; 49: 1598
[5] (刘允中, 李志龙, 顾才鑫. 金属学报, 2013; 49: 1598)
[6] Dumont D, Deschamps A, Brechet Y.Acta Mater, 2004; 52: 2529
[7] Deschamps A, Brechet Y.Scr Mater, 1998; 39: 1517
[8] Thomson D S, Subramanya B S, Levy S A.Metall Trans, 1971; 2: 1149
[9] Conserva M, Russo E D, Caloni O.Metall Trans, 1971; 2: 1227
[10] Gong H, Wu Y X, Liao K.J Mater Eng, 2010; (1): 42
[10] (龚海, 吴运新, 廖凯. 材料工程, 2010; (1): 42)
[11] Davydov V G, Ber L B, Ananiev V N.In: Fridlyander I N ed., Proc 5th Int Conf on Aluminum Alloys, Amsterdam: Kluwer Academic Publishers-Plenum Publishers, 1996: 859
[12] Alekseev A A, Ber L B.Light Alloys Technol, 1993; 5: 18
[13] Archambault P, Godard D.Scr Mater, 2000; 42: 675
[14] Li S L, Huang Z Q, Chen W P, Liu Z M, Qi W J.Trans Mater Heat Treat, 2013; 34(4): 57
[14] (李慎兰, 黄志其, 陈维平, 刘志铭, 戚文军. 材料热处理学报, 2013; 34(4): 57)
[15] Wang G, Yin Z M, Zhao K, Duan J Q, Liu B, Shang B C.Mater Sci Technol, 2011; 19(4): 84
[15] (王岗, 尹志民, 赵凯, 段佳琦, 刘博, 商宝川. 材料科学与工艺, 2011; 19(4): 84)
[16] Robinson J S, Cudd R L, Tanner D A.J Mater Process Technol, 2001; 119: 261
[17] Chen L, Yu Y N.Phase Transformations in Metals and Alloys. Beijing: Higher Education Press, 2011: 233
[17] (陈冷, 余永宁. 金属和合金中的相变. 北京: 高等教育出版社, 2011: 233)
[18] Staley J T.Mater Sci Technol, 1987; 3: 923
[19] Christian J W.The Theory of Transformations in Metals and Alloys. Oxford: Pergamon Press, 1975: 58
[20] Liu S D, Zhang X M, You J H, Huang Z B, Zhang C, Zhang X Y.Trans Nonferrous Met Soc China, 2006; 12: 2034
[20] (刘胜胆, 张新明, 游江海, 黄振宝, 张翀, 张小艳. 中国有色金属学报, 2006; 12: 2034)
[21] Li P Y, Xiong B Q, Zhang Y A, Li Z H, Zhu B H, Wang F, Liu H W.Trans Nonferrous Met Soc China, 2011; 21: 513
[21] (李培跃, 熊柏青, 张永安, 李志辉, 朱宝宏, 王锋, 刘红伟. 中国有色金属学报, 2011; 21: 513)
[22] Liu W J.PhD Dissertation, Central South University, Changsha, 2011
[22] (刘文军. 中南大学博士学位论文, 长沙, 2011)
[23] Chen H.Master Thesis, Central South University, Changsha, 201
[23] (陈慧. 中南大学硕士学位论文, 长沙, 2012)
[24] Dai X Y.PhD Dissertation, Central South University, Changsha, 2008
[24] (戴晓元. 中南大学博士学位论文, 长沙, 2008)
[25] Godard D, Archambault P, Aeby-Gautier E. Acta Mater, 2002; 50: 2319
[26] Tang J G, Chen H, Zhang X M, Liu S D, Liu W J, Ouyang H, Li H P.Trans Nonferrous Met Soc China, 2012; 22: 1255
[27] Tian F Q, Cui J Z.Trans Nonferrous Met Soc China, 2006; 16: 958
[27] (田福泉, 崔建忠. 中国有色金属学报, 2006; 16: 958)
[1] 刘兴军, 魏振帮, 卢勇, 韩佳甲, 施荣沛, 王翠萍. 新型钴基与Nb-Si基高温合金扩散动力学研究进展[J]. 金属学报, 2023, 59(8): 969-985.
[2] 陈礼清, 李兴, 赵阳, 王帅, 冯阳. 结构功能一体化高锰减振钢研究发展概况[J]. 金属学报, 2023, 59(8): 1015-1026.
[3] 冯艾寒, 陈强, 王剑, 王皞, 曲寿江, 陈道伦. 低密度Ti2AlNb基合金热轧板微观组织的热稳定性[J]. 金属学报, 2023, 59(6): 777-786.
[4] 王长胜, 付华栋, 张洪涛, 谢建新. 冷轧变形对高性能Cu-Ni-Si合金组织性能与析出行为的影响[J]. 金属学报, 2023, 59(5): 585-598.
[5] 李民, 王继杰, 李昊泽, 邢炜伟, 刘德壮, 李奥迪, 马颖澈. Y对无取向6.5%Si钢凝固组织、中温压缩变形和软化机制的影响[J]. 金属学报, 2023, 59(3): 399-412.
[6] 王虎, 赵琳, 彭云, 蔡啸涛, 田志凌. 激光熔化沉积TiB2 增强TiAl基合金涂层的组织及力学性能[J]. 金属学报, 2023, 59(2): 226-236.
[7] 唐伟能, 莫宁, 侯娟. 增材制造镁合金技术现状与研究进展[J]. 金属学报, 2023, 59(2): 205-225.
[8] 李赛, 杨泽南, 张弛, 杨志刚. 珠光体-奥氏体相变中扩散通道的相场法研究[J]. 金属学报, 2023, 59(10): 1376-1388.
[9] 李会朝, 王彩妹, 张华, 张建军, 何鹏, 邵明皓, 朱晓腾, 傅一钦. 搅拌摩擦增材制造技术研究进展[J]. 金属学报, 2023, 59(1): 106-124.
[10] 卢海飞, 吕继铭, 罗开玉, 鲁金忠. 激光热力交互增材制造Ti6Al4V合金的组织及力学性能[J]. 金属学报, 2023, 59(1): 125-135.
[11] 高栋, 周宇, 于泽, 桑宝光. 液氮温度下纯Ti动态塑性变形中的孪晶变体选择[J]. 金属学报, 2022, 58(9): 1141-1149.
[12] 马志民, 邓运来, 刘佳, 刘胜胆, 刘洪雷. 淬火速率对7136铝合金应力腐蚀开裂敏感性的影响[J]. 金属学报, 2022, 58(9): 1118-1128.
[13] 沈岗, 张文泰, 周超, 纪焕中, 罗恩, 张海军, 万国江. 热挤压Zn-2Cu-0.5Zr合金的力学性能与降解行为[J]. 金属学报, 2022, 58(6): 781-791.
[14] 余春, 徐济进, 魏啸, 陆皓. 核级镍基合金焊接材料失塑裂纹研究现状[J]. 金属学报, 2022, 58(4): 529-540.
[15] 徐流杰, 宗乐, 罗春阳, 焦照临, 魏世忠. 难熔高熵合金的强韧化途径与调控机理[J]. 金属学报, 2022, 58(3): 257-271.