1.4%C-1.4%Cr鋼等温马氏体形成的金相研究 |
徐祖耀;朱钰如;王蓉蓉 |
上海交通大学;上海交通大学;上海交通大学 |
|
METALLOGRAPHIC INVESTIGATION OF ISOTHERMAL MARTENSITE FORMATION IN A 1.4%C-1.4% Cr STEEL |
HSU TZU-YAO; TSU CHUEH-JU; WANG YUNG-YUNG(Shanghai Chiao Tung University) |
引用本文:
徐祖耀;朱钰如;王蓉蓉. 1.4%C-1.4%Cr鋼等温马氏体形成的金相研究[J]. 金属学报, 1964, 7(4): 437-441.
,
,
.
METALLOGRAPHIC INVESTIGATION OF ISOTHERMAL MARTENSITE FORMATION IN A 1.4%C-1.4% Cr STEEL[J]. Acta Metall Sin, 1964, 7(4): 437-441.
[1] #12 [2] 张沛霖、徐萃章:金属学报,1956,1,347. [3] Ko, T. (柯俊), Edmondson, B.: Acta Met., 1954, 2, 235. [4] #12 [5] Das Gupta, S. C., Lement, B. S.: Trans. AIME, 1951, 191, 727. [6] Machlin, E. S., Cohen, M.: Trans, AIME, 1952, 194, 489. [7] Kaufman, L., Cohen, M.: Progress in Metal Physics, (Pergamon, 1958) , vol. 7, p. 235-241.! |
|