金属学报  2013, Vol. 49 Issue (8): 932-938    DOI: 10.3724/SP.J.1037.2013.00112
  论文 本期目录 | 过刊浏览 |
多向压缩中AZ31镁合金变形行为的EBSD跟踪研究
黄洪涛1),Godfrey Andrew1),刘伟1),付宝勤1),刘庆2)
1)清华大学材料学院先进材料教育部重点实验室, 北京100084
2)重庆大学材料科学与工程学院,重庆400044
DEFORMATION BEHAVIOR OF AZ31 MAGNESIUM ALLOY DURING MULTIAXIAL COMPRESSION BY EBSD TRACKING
HUANG Hongtao1), Godfrey Andrew1), LIU Wei1), FU Baoqin1),LIU Qing2)
1)Key Laboratory of Advanced Materials (MOE), School of Materials Science and Engineering, Tsinghua University, Beijing 100084
2)School of Materials Science and Engineering, Chongqing University, Chongqing 400044
引用本文:

黄洪涛,Godfrey Andrew,刘伟,付宝勤,刘庆. 多向压缩中AZ31镁合金变形行为的EBSD跟踪研究[J]. 金属学报, 2013, 49(8): 932-938.
HUANG Hongtao, Godfrey Andrew, LIU Wei, FU Baoqin, LIU Qing. DEFORMATION BEHAVIOR OF AZ31 MAGNESIUM ALLOY DURING MULTIAXIAL COMPRESSION BY EBSD TRACKING[J]. Acta Metall Sin, 2013, 49(8): 932-938.

全文: PDF(3417 KB)  
摘要: 

利用显微硬度点法结合电子背散射衍射(EBSD)技术,跟踪研究了多向压缩路径下AZ31镁合金的变形行为.采用先沿板材横向(TD)压缩然后沿板材法向(ND)进行压缩的应变路径.结果表明,绝大多数晶粒TD压缩变形中主要以{1012}拉伸孪生为主,ND压缩变形过程中主要以退孪生为主,少数晶粒变形行为不同的原因是由于其初始取向偏离基面织构太大.在ND压缩变形中发生退孪生行为的晶粒内, 没有发现新的孪生变体出现,表明退孪生比激活一个新的孪生变体要容易. 剩余孪晶面积分数减少到0时,ND压缩变形中的局部区域应变小于TD压缩变形,表明完全退孪生所需应变比孪生小.

关键词 AZ31镁合金拉伸孪生退孪生局部区域应变EBSD跟踪研究    
Abstract

Cross rolling and multidirectional forging deformation modes are effective methods to improve the plastic forming ability of magnesium alloy. In these plastic forming process, multi-directional compression deformation is often involved. In this study, the deformation behavior during multi-directional compression of a AZ31 magnesium alloy was investigated using a micro-grid method in combination with electron backscatter diffraction (EBSD) tracking method. The sheets were compressed along transverse direction (TD) followed by compression along normal direction (ND). The experimental results show that {1012}<1011> tensile twinning dominates the deformation process during initial compression along TD, and that for most grains detwinning of these {1012}<1011> tensile twins dominates the deformation process during a following compression along ND. For some grains with a large deviation from the basal texture, a different deformation behavior is seen. No new twin variants are found in grains that underwent detwinning during compression along ND. This indicates that detwinning of {1012}<1011> tensile twins is favored over the activation of a different twin variants during deformation of the AZ31 magnesium alloy. The remaining twin area fraction can reduce to near-zero even when the local strain subjected during ND compression is less than that subjected during the initial TD
compression, demonstrating that a smaller strain is required for detwinning than for the initial twinning.

Key wordsAZ31 magnesium alloy    extension twinning, detwinning    local strain    EBSD tracking
收稿日期: 2013-03-11     
基金资助:

国家重点基础研究发展计划资助项目2007CB613703

作者简介: 黄洪涛,男, 1983年生, 博士生

[1]Lou X Y, Li M, Boger R K, Agnew S R, Wagoner R H.Int J Plast, 2007; 23: 44
[2]Liu Q. Acta Metall Sin, 2010; 46: 1458
(刘庆. 金属学报, 2010; 46: 1458)
[3]Barnett M R. Mater Sci Eng, 2007; A464: 1
[4]Barnett M R. Mater Sci Eng, 2007; A464: 8
[5]Martin E, Capolungo L, Jiang L, Jonas J J. Acta Mater, 2010; 58: 3970
[6]Luo J R, Godfrey A, Liu W, Liu Q. Acta Mater, 2012;60: 1986
[7]Luo J R, Liu Q, Liu W, Godfrey A. Acta Metall Sin,2011; 47: 1567
(罗晋如, 刘庆, 刘伟, Godfrey A. 金属学报, 2011; 47:1567)
[8]Luo J R, Liu Q, Liu W, Godfrey A. Acta Metall Sin,2012; 48: 717
(罗晋如, 刘庆, 刘伟, Godfrey A. 金属学报, 2012; 48:717)
[9]Huang H T, Liu W, Godfrey A, Tang R H, Liu Q. Acta Metall Sin, 2012; 48: 357
(黄洪涛, 刘伟, Godfrey A, 唐瑞鹤, 刘庆. 金属学报,2012; 48: 357)
[10]Wang Y N, Huang J C. Acta Mater, 2007; 55: 897
[11]Proust G, Tome C N, Jain A, Agnew S R. Int JPlast, 2009; 25: 861
[12]Chapelle D, Darrieulat M. Mater Sci Eng, 2003;A347: 32
[13]Lineau C, Rey C, deLesegno P V. Mater Sci Eng,1997; A234: 853
[14]Delaire F, Raphanel J L, Rey C. Acta Mater, 2000;48: 1075
[15]Barnett M R, Jacob S, Gerard B F, Mullins J G. Scr Mater, 2008; 59: 1035
[16]Allais L, Bornert M, Bretheau T, Caldemasion D.Acta Mater, 1994; 42: 3865
[17]Huang H T,PhD Dissertation, Tsinghua University,Beijing, 2013
(黄洪涛. 清华大学博士学位论文, 北京, 2013)
[18]Huang H T, Godfrey A, Liu W, Tang R H, Liu Q. Acta Metall Sin, 2012; 48: 915
(黄洪涛, Godfrey A, 刘伟, 唐瑞鹤, 刘庆. 金属学报,2012; 48: 915)
[19]Nave M D, Barnett M R. Scr Mater, 2004; 51: 881
[20]Yang X Y, Zhang L. Acta Metall Sin, 2009; 45: 1303
(杨续跃, 张雷. 金属学报, 2009; 45: 1303)
[21]Brown D W, Agnew S R, Bourke M A M, Holden T M, Vogel S C,Tome C N. Mater Sci Eng, 2005; A399: 1
[22]Clausen B, Tome C N, Brown D W, Agnew S R. Acta Mater, 2008; 56: 2456
[23]Lou C, Zhang X Y, Wang R H, Duan G L, Liu Q. Acta Metall Sin, 2013; 49: 291
(娄超,张喜燕, 汪润红, 段高林, 刘庆.金属学报, 2013; 49: 291)
[24]Wu L, Agnew S R, Brown D W, Stoica G M, Clausen B, Jain A,Fielden D E, Liaw P K. Acta Mater, 2008; 56: 3699
[25]Wu L, Jain A, Brown D W, Stoica G M, Agnew S R, Clausen B,Fielden D E, Liaw P K. Acta Mater, 2008; 56: 688

 

[1] 周红伟, 高建兵, 沈加明, 赵伟, 白凤梅, 何宜柱. 高温低周疲劳下C-HRA-5奥氏体耐热钢中孪晶界演变[J]. 金属学报, 2022, 58(8): 1013-1023.
[2] 陈扬, 毛萍莉, 刘正, 王志, 曹耕晟. 高速冲击载荷下预压缩AZ31镁合金的退孪生行为与动态力学性能[J]. 金属学报, 2022, 58(5): 660-672.
[3] 王雪梅, 殷正正, 于晓彤, 邹玉红, 曾荣昌. AZ31镁合金表面苯丙氨酸、甲硫氨酸和天冬酰胺诱导Ca-P涂层耐蚀性能比较[J]. 金属学报, 2021, 57(10): 1258-1271.
[4] 韩林原, 李旋, 储成林, 白晶, 薛烽. 流场环境中AZ31镁合金的腐蚀行为研究[J]. 金属学报, 2017, 53(10): 1347-1356.
[5] 闫亚琼,罗晋如,张济山,庄林忠. 强织构AZ31镁合金板材深低温轧制过程中微观组织演变及力学性能控制研究[J]. 金属学报, 2017, 53(1): 107-113.
[6] 白敬胜,卢秋虹,卢磊. 纳米孪晶Cu中局部剪切应变诱导的退孪生行为*[J]. 金属学报, 2016, 52(4): 491-496.
[7] 汪炳叔,邓丽萍,CHAPUIS Adrien,郭宁,李强. AZ31镁合金在平面应变压缩过程中的孪生行为研究*[J]. 金属学报, 2015, 51(12): 1441-1448.
[8] 娄超,张喜燕,汪润红,段高林,刘庆. 退孪生行为以及{1012},孪晶片层结构对镁合金力学性能的影响[J]. 金属学报, 2013, 49(3): 291-296.
[9] 黄洪涛 Godfrey Andrew 刘伟 唐瑞鹤 刘庆. 样品取向对AZ31镁合金静态再结晶行为的影响[J]. 金属学报, 2012, 48(8): 915-921.
[10] 孙朝阳 栾京东 刘赓 李瑞 张清东. AZ31镁合金热变形流动应力预测模型[J]. 金属学报, 2012, 48(7): 853-860.
[11] 罗晋如,刘庆,刘伟,Godfrey Andrew. 轧制温度对AZ31镁合金轧制板材中的{1011}-{1012}双孪生行为的影响[J]. 金属学报, 2012, 48(6): 717-724.
[12] 黄洪涛 刘伟 A. Godfrey 唐瑞鹤 刘庆. AZ31镁合金单轴压缩中孪生行为研究[J]. 金属学报, 2012, 48(3): 357-362.
[13] 罗晋如 刘庆 刘伟 Godfrey Andrew. AZ31镁合金板轧制过程中的{10-11}-{10-12}双孪生对板材显微组织、织构、力学性能的影响[J]. 金属学报, 2011, 47(12): 1567-1574.
[14] 王东 刘杰 肖伯律 马宗义. 铝合金/镁合金搅拌摩擦焊接界面处Mg/Al反应及接头力学性能[J]. 金属学报, 2010, 46(5): 589-594.
[15] 高英俊 罗志荣 胡项英 黄创高. 相场方法模拟AZ31镁合金的静态再结晶过程[J]. 金属学报, 2010, 46(10): 1161-1172.