金属学报  2010, Vol. 46 Issue (6): 708-714    DOI: 10.3724/SP.J.1037.2009.00600
  论文 本期目录 | 过刊浏览 |
DZ468合金高周疲劳性能研究
刘恩泽; 郑志; 佟 健; 宁礼奎; 管秀荣
中国科学院金属研究所; 沈阳 110016
STUDY ON HIGH CYCLE FATIGUE PROPERTIES OF DZ468 SUPERALLOY
LIU Enze; ZHENG Zhi; TONG Jian; NING Likui; GUAN Xiurong
Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016
引用本文:

刘恩泽 郑志 佟健 宁礼奎 管秀荣. DZ468合金高周疲劳性能研究[J]. 金属学报, 2010, 46(6): 708-714.
. STUDY ON HIGH CYCLE FATIGUE PROPERTIES OF DZ468 SUPERALLOY[J]. Acta Metall Sin, 2010, 46(6): 708-714.

全文: PDF(2643 KB)  
摘要: 

本文研究了新型镍基高温合金DZ468的高周疲劳性能. 结果表明: 当应力比R=-1时, 在900和760 ℃条件下, DZ468合金的疲劳强度分别为290和300 MPa. DZ468合金的高周疲劳试样断口由疲劳源、疲劳区和瞬断区组成. 裂纹在表面、次表面和内部缺陷部位萌生, 裂纹扩展具有第I和第II阶段, 随应力幅增加裂纹扩展速率增大. 光滑试样的疲劳裂纹扩展方式与变形机制间存在一定的关系, 位错的平面滑移、交滑移和攀移的共同作用导致 了合金在900和760℃时裂纹扩展具有两个 阶段.

关键词 镍基高温合金 高周疲劳性能 断口    
Abstract

The high cycle fatigue properties of a new type Ni-based superalloy DZ468 were investigated in this paper. The high cycle fatigue strengths of DZ468 alloy at 900 and 760 ℃ with a ratio of stress R=-1 reach 290 and 300 MPa, respectively. The high cycle fatigue fractures of DZ468 alloy were composed of fatigue source, fatigue district and final stage. Cracks originate from surface, sub-surface and inner defect of sample. At 900 and 760 ℃, stage I and stage II crack propagation could be observed from fatigue fracture, which was caused by the combination action of planar slip, cross slip and climb of dislocations. With increasing of stress value, the crack propagation rate quickly increase. A correlation exists between the crack propagation mode and deformation mode.

Key wordsNi-based superalloy    high cycle fatigue property    fracture
收稿日期: 2009-09-10     
作者简介: 刘恩泽, 男, 1976年生, 助理研究员, 博士

[1] Yu Z F, Zheng Z, Liu E Z, Yu Y S, Zhu Y X. J Chin Soc Corros Prot, 2008; 28: 277
(于忠峰, 郑志, 刘恩泽, 于永泗, 朱耀宵. 中国腐蚀与防护学报, 2008; 28: 277)
[2] Ning L K, Zheng Z, Tan Y, Liu E Z, Tong J, Yu Y S, Wang H. Acta Metall Sin, 2009; 45: 161
(宁礼奎, 郑 志, 谭 毅, 刘恩泽, 佟健, 于永泗, 王华. 金属学报, 2009; 45: 161)
[3] Liu E Z, Sun S C, Tu G F, Zheng Z, Ning L K, Zhang L F. Acta Metall Sin, 2009; 45: 1217
(刘恩泽, 孙树臣, 涂赣峰, 郑 志, 宁礼奎, 张凌峰. 金属学报, 2009; 45: 1217)
[4] Hoffelner W. Metall Trans, 1982; 13A: 1245
[5] Sajjadi S A, Nategh S. Mater Sci Eng, 2001; A307: 158
[6] Liu Y, Yu J J, Xu Y. Mater Sci Eng, 2007; A454: 357
[7] Hoffelner W, Gudmundson P. Eng Fract Mech, 1982; 16: 365
[8] Jones B F. Int J Fatigue, 1984; 6: 75
[9] Pope D P, Ezz S S. Int Met Rev, 1984; 29: 136
[10] Sieborger D, Knake H, Glatzel U. Mater Sci Eng, 2001; A298: 26
[11] Shi C X, Yan M G, Zhu Z Q. China Aeronautical Materials Handbooks. Beijing: China Standard Press, 2001: 550
(师昌绪, 颜鸣皋, 朱之琴. 中国航空材料手册, 北京: 中国标准出版社, 2001: 550)
[12] Zheng Y R, Cai Y L, Ruan Z C, Ma S. J Aeronaut Mater, 2006; 26: 25
(郑运荣, 蔡玉林, 阮中慈, 马书. 航空材料学报, 2006; 26: 25)
[13] Zheng Y R, Wang Yu P, Xie J H, Caron P, Khan T. In: Reichman S, Duhl D N, Maurer G, Antolovich S eds., Superalloys 1988, PA: TMS, 1988: 335
[14] Zheng Y R, Cai Y L, Ruan Z C. Acta Metall Sin, 1987; 23: A430
(郑运荣, 蔡玉林, 阮中慈. 金属学报, 1987; 23: A430)
[15] Zheng Y R, Cai Y L, Wang L B. Acta Metall Sin, 1983; 19: A190
(郑运荣, 蔡玉林, 王罗宝. 金属学报, 1983; 19: A190)
[16] Zheng Y R. Chin J Aeronaut, 198; 7: 482
(郑运荣. 航空学报, 1986; 7: 482)
[17] Gell M, Leverant G R. Acta Metall, 1968; 16: 553
[18] Bowen A W, Forsyh P J EMater Sci Eng, 1981; 49: 141
[19] Forsyth P J E. Acta Metall, 1963; 11: 703
[20] Laird C. Fatigue Crack Propagation, STP415. Philadelphia: ASTM, 1967: 131
[21] Liu Y. PhD Thesis, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2008
(刘 源. 中国科学院金属研究所博士学位论文, 沈阳, 2008)
[22] Chu Z K. PhD Thesis, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2008
(储昭贶. 中国科学院金属研究所博士学位论文, 沈阳, 2008)

[1] 王磊, 刘梦雅, 刘杨, 宋秀, 孟凡强. 镍基高温合金表面冲击强化机制及应用研究进展[J]. 金属学报, 2023, 59(9): 1173-1189.
[2] 郑亮, 张强, 李周, 张国庆. /降氧过程对高温合金粉末表面特性和合金性能的影响:粉末存储到脱气处理[J]. 金属学报, 2023, 59(9): 1265-1278.
[3] 江河, 佴启亮, 徐超, 赵晓, 姚志浩, 董建新. 镍基高温合金疲劳裂纹急速扩展敏感温度及成因[J]. 金属学报, 2023, 59(9): 1190-1200.
[4] 穆亚航, 张雪, 陈梓名, 孙晓峰, 梁静静, 李金国, 周亦胄. 基于热力学计算与机器学习的增材制造镍基高温合金裂纹敏感性预测模型[J]. 金属学报, 2023, 59(8): 1075-1086.
[5] 张禄, 余志伟, 张磊成, 江荣, 宋迎东. GH4169高温合金热机械疲劳循环损伤机理及数值模拟[J]. 金属学报, 2023, 59(7): 871-883.
[6] 袁江淮, 王振玉, 马冠水, 周广学, 程晓英, 汪爱英. Cr2AlC涂层相结构演变对力学性能的影响[J]. 金属学报, 2023, 59(7): 961-968.
[7] 刘来娣, 丁彪, 任维丽, 钟云波, 王晖, 王秋良. DZ445镍基高温合金高温长时间氧化形成的多层膜结构[J]. 金属学报, 2023, 59(3): 387-398.
[8] 于少霞, 王麒, 邓想涛, 王昭东. GH3600镍基高温合金极薄带的制备及尺寸效应[J]. 金属学报, 2023, 59(10): 1365-1375.
[9] 祝国梁, 孔德成, 周文哲, 贺戬, 董安平, 疏达, 孙宝德. 选区激光熔化 γ' 相强化镍基高温合金裂纹形成机理与抗裂纹设计研究进展[J]. 金属学报, 2023, 59(1): 16-30.
[10] 李民, 李昊泽, 王继杰, 马颖澈, 刘奎. 稀土Ce对薄带连铸无取向6.5%Si钢组织、高温拉伸性能和断裂模式的影响[J]. 金属学报, 2022, 58(5): 637-648.
[11] 朱玉平, 盛乃成, 谢君, 王振江, 荀淑玲, 于金江, 李金国, 杨林, 侯桂臣, 周亦胄, 孙晓峰. 高钨镍基高温合金K416BW相的析出行为[J]. 金属学报, 2021, 57(2): 215-223.
[12] 刘超, 姚志浩, 江河, 董建新. GH4720Li合金毫米级粗大晶粒热变形获得均匀等轴晶粒的可行性及工艺控制[J]. 金属学报, 2021, 57(10): 1309-1319.
[13] 张小丽, 冯丽, 杨彦红, 周亦胄, 刘贵群. 二次枝晶取向对镍基高温合金晶粒竞争生长行为的影响[J]. 金属学报, 2020, 56(7): 969-978.
[14] 张北江,黄烁,张文云,田强,陈石富. 变形高温合金盘材及其制备技术研究进展[J]. 金属学报, 2019, 55(9): 1095-1114.
[15] 金辰日, 杨素媛, 邓学元, 王扬卫, 程兴旺. 纳米晶化对锆基非晶合金动态压缩性能的影响[J]. 金属学报, 2019, 55(12): 1561-1568.